Anti iron tip erosion super low Ag flux cored wire solder

S01X7Ca-72M
Sn 0.1Ag 0.7Cu+Co

 
 
0.1%Ag for
Longer-lasting Iron Tips

Inhibits erosion of Fe plating

Co added to S01X7Ca-72M forms a barrier layer at the iron tip surface,
which inhibits erosion of the tip. S01X7Ca-72M significantly reduces wear of iron tips compared to regular lead-free solder.

Prevents bridging in slide soldering

72M series contain new activators for improved wettability and new resin composition for better flux coverage.
They can prevent bridging even at defect prone conditions such as low iron tip temperature or fast sliding speed.

■Image of slide soldering

Ultimate cost reduction by flux-cored solder

Ag content of S01X7Ca-72M is 0.1%. Absolutely low Ag content achieves significant cost reduction,
assisting realization of ultimate cost reduction along with its erosion inhibition effect.

Product Performance Table

Product Name
S01X7Ca-72M
Product Category
Flux Cored Solder Wire
Melting Point(℃)
217-227
Flux Content(%)
3.2
Halide content(%)
< 0.01
Flux Type
ROL0 (IPC J-STD-004)
Diameter(mm φ)
0.3, 0.5, 0.6, 0.8, 1.0 ,1.2

You have question?